(CN105154791) 1. A bead mill using high hardness and high toughness abrasion resistant ball, characterized in, its component by weight percent comprising: The remainder being iron and incidental impurities; During the manufacture, will scrap, iron alloys, manganese ingots, ferromolybdenum, gray cast iron, enameled wire scrap charged into a furnace heated as a base material, and when the temperature was raised to 800-1000 Ć, 1.5-3 h incubation, addition of a deoxidizing agent retained for 2-4min, into a mold, forging, obtaining the substrate, the substrate is preheated to 600-800 Ć hammering 15-30min, cooled to 700-750 Ć, quenching, the tempering process, the material is uniform stalls are mounted on the basket, loaded into the resistance furnace at room temperature, to 30-45 Ć/h after raising to 560 Ć, 0.5-1 h incubation, wherein when the temperature was raised to 350 Ć, 400 Ć, 480 Ć, 560 Ć are respectively given 20-40min, 30-60min, 20-60min, 30-50min insulation, and then to 50-80 Ć/h at a rate of the furnace temperature was raised to a temperature of 800-900 Ć for warming, incubated for 1-3h, and placed on an iron frame held fast air cooling, tempering, annealing temperature is 240-280 Ć, a tempering time of 2-3h, obtained using high hardness and high toughness wearable ball mill.
最新评论
暂无评论。